Glass Yarn

Application:
ConstitutionofSize:BSXXXXW.RwaterblockingW; non-waterblockingRdensityofyarnshortnameofglassyarn SIZEINNDERDIAMETER(W2)mm HIGHTOFCORE(H1)mm THICKNESSOFCOREmm HIGHTOFYARN(H2)mm OUTERDIAMETEROFYARN(W1)mmN.WOF...
  • Detail



 

Constitution of Size:

BS  XXXX  W . R

waterblocking Wnon-waterblocking R

 

density of yarn

 

                           short name of glass yarn


图片1.png


SIZE

INNDER DIAMETER(W2) mm

HIGHT OF CORE

(H1) mm

THICKNESS OF CORE

mm

HIGHT OF YARN

(H2) mm

OUTER DIAMETER OF YARN

(W1) mm

N.W OF YARN

kg

LENGTH OF YARN

km/roll

BS600R

94

220/275

7.0

200/254

240

customers requirement

customers requirement

BS785R

94

220/275

7.0

200/254

240

customers requirement

customers requirement

BS1200R

94

220/270

7.0

200/254

240

customers requirement

customers requirement

BS2400R

94

220/275

7.0

200/254

240

customers requirement

customers requirement

BSZ600W

94

220/275

7.0

200/254

240

customers requirement

customers requirement

BSZ785W

94

220/275

7.0

200/254

240

customers requirement

customers requirement

BSZ1200W

94

220/275

7.0

200/254

240

customers requirement

customers requirement

BSZ2400W

94

220/275

7.0

200/254

240

customers requirement

customers requirement

 

Property:

SIZE

UNIT

BS.R

-600D

BS.R

-785D

BS.R

-1200D

BS.R

-2400D

BS.W

-600D

BS.W

-785D

BS.W

-1200D

BS.W

-2400D

LINEAR DENSITY

Tex

600

±10%

785

±10%

1200

±10%

2400

±10%

600

±10%

785

±10%

1200

±10%

2400

±10%

DENSITY

g/cm3

2.55

±0.05

2.55

±0.05

2.55

±0.05

2.55

±0.05

2.55

±0.05

2.55

±0.05

2.55

±0.05

2.55

±0.05

TENSILE STRENGTH

1) BREAK

2) LASE 0.3%

3) LASE 0.5%

4) LASE 1.0%

 

 

 

N

 

Min.350

Min.45

 

Min.80

 

Min.170

 

Min.450

Min.55

 

Min.95

 

Min.195

 

Min.600

Min.90

 

Min.160

 

Min.340

 

 

 

 

Min.320

 

 

Min.350

Min.45

 

Min.80

 

Min.170

 

Min.450

Min.55

 

Min.95

 

Min.195

 

Min.600

Min.90

 

Min.160

 

Min.340

 

 

 

 

Min.320

 

ELONGATION AT BREAK

%

Min.2.0

Min.2.0

Min.2.0

Min.2.0

Min.2.0

Min.2.0

Min.2.0

Min.2.0

Y. MODULUS

Gpa

Min.70

Min.70

Min.70

Min.70

Min.70

Min.70

Min.70

Min.70

EXPANSION RATE

%

N/A

N/A

N/A

N/A

Min.500

Min.500

Min.500

Min.500

HEAT-RESISTANCE EXPANSION RATE

%

N/A

N/A

N/A

N/A

Min.500

Min.500

Min.500

Min.500